metallized capacitor film

Al-Zn Metallized polyester & Polypropylene film
types of metallized layer
Metallized film for capacitors used
Wave cut metallized polypropylene & Polyester film
types of metallized layer [Mar 29,2016]
types of metallized layer
Products:
1. Aluminum metallized polypropylene film.
2.Aluminum metallized polypropylene safety film.
3.Zinc - Aluminum alloy metallized polypropylene film with heavy edge.
4. Zinc - Aluminum alloy metallized polypropylene safety film with heavy edge.
5.Zinc - Aluminum alloy metallized polypropylene film with heavy edge and slope metallized film.
6.Aluminum metallized polyester film.
7.Zinc - Aluminum alloy metallized polyester film with heavy edge.
8.Zinc-Aluminum Alloy metallized polypropylene film with high ssquare resistance
9. According to customer requirement design to producing all kinds of metallized film for capacitor used.

Cores:
1.Material:Plastic.
2.Width:Film Slit Width ±0.3mm.
3.Inner Diameter:75mm +1.0mm/-0.5mm.

Roll Outer Diameter:
     Slit widths(W)Recommend outer diameter(D)
4.5mm≤W<10mm140mm≤D≤185mm
10mm≤W<25mm 150mm≤D≤185mm
25mm≤W<50mm   150mm≤D≤240mm 
50mm≤W150mm≤D≤350mm  

Specifications of metallized film:
1)Metallized polypropylene film  

Properties

Unit

Requirements
Densityg/cm30.905±0.005
 Thicknessµm3.8 ~ 15

Tensile Strength
MD
(MPa)
≥100

Elongation at Break
MD
(%)
40 ~ 200

Heat Shrinkage
MD
(%)
≤5 ( 120°C, 10min)
( 120°C , 10 min )

Break-dowm voltage
V/µm≥350 ( 23°C, DC )

Coating square resistance
 Al1.5±0.52.0±0.52.5±0.53±1

Zn/Al
(heavy-edge area):3±1
(non heavy-edge area):(6~7.5)±30%
 with gradient square (heavy-edge area):3±1
(non heavy-edge area):(2~20)

Dissipation Factor
-≤4×10-4 (20ºC,1KHz )
RCΩF≥5×104

2.)Metallized polyester Film

Properties

Unit

Requirements
Densityg/cm31.34
 Thicknessµm<55~12>12

Tensile Strength
MD
(MPa)
≥84≥108≥120

Elongation at Break
MD
(%)
≥22≥33≥44

Break-dowm voltage
V/µm≥200 
( 23°C, DC )
≥250 
( 23°C, DC )

Heat Shrinkage
MD
(%)
≤3 ( 120°C, 10min)

Coating square resistance
 Al1.5±0.52.0±0.52.5±0.53±1

Zn/Al
(heavy-edge area):3±1
(non heavy-edge area):(6~7.5)±30%

Dissipation Factor
-≤60×10-4 (20ºC,1KHz )
RCΩF≥1×104

Note: Coating square resistance annotation is a typical value,can be customized.

Packing:
1. Roll films are packed in vacuum plastic bag and heat-sealed with desiccants.
2.Bags are marked with lables of types
3. The bags are packed in carton cases.
4.The cartons are wrapped in wooden cases or reinforced carton.


Storge:
1. Metallized film should be stored in its original package until its use with temperature  5 ~ 35ºC and humidity less than 85%RH.
2. Metallized layer is easily oxidized when exposure to moisture. Therefore, the film should be used as soon as possible when opened. 
 
3.The recommended temperature is 15 -25ºC with humidity less than 60%RH after the package is open.
 
4.With original sealed package, and stored in the above mentioned conditions, the storage time can be as following: 
Al metalized Film: 12 months from the delivered date..
Al/Zn Alloy metalized Film: As Zn is relatively unstable, preservation period(from delivery date) depends on the resistance of the film:
≤10 Ω/: 6 months 
10 ~15Ω/: 3 months 
>15Ω/: 1months 
 