Al Zn Metallized Polypropylene Capacitor Mpp Film

• Customization: Available
• Usage: Capacitor Use
• Type: Metallized Film
• Model NO.: mpp film
• Material: BOPP
• Feather: Mositure Proof
• Hardness: Soft
• Transparency: Opaque
• Processing Type: Multiple Extrusion
• Thickness: 3.6-12um
• Width: 4.5-620mm
• Types of Matallized Layer: Al/Zn Metallized Film, Al Metllized Film,
• Density: 0.905+/-0.005 g/cm3
• Margin Value: 0.5mm 1mm 1.5mm 2mm 2.5mm
• Transport Package: Capacitor Film International Standard Package
• Specification: ISO9001, SGS, CQC, RHoS
• Trademark: CSF
• Origin: Anhui China
• HS Code: 3921909090
• Production Capacity: 100 Tons Per Month

Product Description

Al Zn Metallized Polypropylene Capacitor MPP Film




Products:
1. Aluminum metallized polypropylene film.
2.Aluminum metallized polypropylene safety film.
3.Zinc - Aluminum alloy metallized polypropylene film with heavy edge.
4. Zinc - Aluminum alloy metallized polypropylene safety film with heavy edge.
5.Zinc - Aluminum alloy metallized polypropylene film with heavy edge and slope metallized film.
6.Aluminum metallized polyester film.
7.Zinc - Aluminum alloy metallized polyester film with heavy edge.
8.Zinc-Aluminum Alloy metallized polypropylene film with high ssquare resistance
9. According to customer requirement design to producing all kinds of metallized film for capacitor used.

Cores:
1.Material:Plastic.
2.Width:Film Slit Width ±0.3mm.
3.Inner Diameter:75mm +1.0mm/-0.5mm.

Roll Outer Diameter:

Slit widths(W)	Recommend outer diameter(D)
4.5mm≤W<10mm	140mm≤D≤185mm
10mm≤W<25mm	150mm≤D≤185mm
25mm≤W<50mm	150mm≤D≤240mm
50mm≤W	150mm≤D≤350mm

Specifications of metallized film:
1)Metallized polypropylene film  

Properties	Unit	Requirements
Density	g/cm3	0.905±0.005
Thickness	µm	3.8 ~ 15
Tensile Strength	MD (MPa)	≥100
Elongation at Break	MD (%)	40 ~ 200
Heat Shrinkage	MD (%)	≤5 ( 120°C, 10min) ( 120°C , 10 min )
Break-dowm voltage	V/µm	≥350 ( 23°C, DC )
Coating square resistance		Al	1.5±0.5	2.0±0.5	2.5±0.5	3±1
		Zn/Al	(heavy-edge area):3±1 (non heavy-edge area):(6~7.5)±30%
		with gradient square	(heavy-edge area):3±1 (non heavy-edge area):(2~20)
Dissipation Factor	-	≤4×10-4 (20ºC,1KHz )
RC	ΩF	≥5×104

2.)Metallized polyester Film

Properties	Unit	Requirements
Density	g/cm3	1.34
Thickness	µm	<5		5~12			>12
Tensile Strength	MD (MPa)	≥84		≥108			≥120
Elongation at Break	MD (%)	≥22		≥33			≥44
Break-dowm voltage	V/µm	≥200  ( 23°C, DC )		≥250  ( 23°C, DC )
Heat Shrinkage	MD (%)	≤3 ( 120°C, 10min)
Coating square resistance		Al	1.5±0.5		2.0±0.5	2.5±0.5		3±1
		Zn/Al	(heavy-edge area):3±1 (non heavy-edge area):(6~7.5)±30%
Dissipation Factor	-	≤60×10-4 (20ºC,1KHz )
RC	ΩF	≥1×104

Note: Coating square resistance annotation is a typical value,can be customized.

Packing:
1. Roll films are packed in vacuum plastic bag and heat-sealed with desiccants.
2.Bags are marked with lables of types
3. The bags are packed in carton cases.
4.The cartons are wrapped in wooden cases or reinforced carton.


Storge:
1. Metallized film should be stored in its original package until its use with temperature  5 ~ 35ºC and humidity less than 85%RH.
2. Metallized layer is easily oxidized when exposure to moisture. Therefore, the film should be used as soon as possible when opened. 
 
3.The recommended temperature is 15 -25ºC with humidity less than 60%RH after the package is open.
 
4.With original sealed package, and stored in the above mentioned conditions, the storage time can be as following: 
Al metalized Film: 12 months from the delivered date..
Al/Zn Alloy metalized Film: As Zn is relatively unstable, preservation period(from delivery date) depends on the resistance of the film:
≤10 Ω/: 6 months 
10 ~15Ω/: 3 months 
>15Ω/: 1months